<span style="font-size:1.2em;font-weight:bold;">IRHD hardness</span>
__FORCETOC__
==General==

The IRHD (International Rubber Hardness Degree) hardness test method was developed specifically for elastomers and thermoplastic elastomers, in which the total deformation at small loads is used to obtain [[Material Value|characteristic values]]. The IRHD hardness is determined in accordance with ISO 48-2, which was derived from ISO 48 as part of the renumbering of hardness testing standards. The predecessors of DIN ISO 48 were DIN 53519-1 and DIN 53519-2.

==Schematic of the test arrangement==

To determine the hardness according to IRHD, a pressure plate is moved without impact until it rests on the test specimen ('''Figure'''). Subsequently, a spherical indenter (ball or pressure rod with spherical tip) is pressed into the test specimen by means of defined forces (contact force and main force). The requirement stated in DIN 53519-1 and -2 that the indenter must be a stainless steel ball is no longer found in subsequent standards.<br>
The indentation depth is indicated on the dial gauge. Due to the design of this test system, it is particularly suitable for determining the hardness of small parts, such as sealing rings or similar.

[[file:irhd1.jpg|400px]]
{| 
|- valign="top"
|width="50px"|'''Figure''': 
|width="600px" |Test arrangement for determining the IRHD hardness
|}

==Classification of the methods==

According to the test standard, the ball indentation hardness IRHD is divided into the methods N (normal test), method H (test at high hardness), method L (test at low hardness) and method M (micro hardness). Essentially, these procedures differ in the diameter of the indentation ball and the load height, whereby these parameters must be selected to suit the respective application. The ball diameters are 2.5 mm for procedure N, 1 mm for procedure H, 5 mm for procedure L and 0.395 mm for procedure M.

The table below shows the different IRHD methods and the corresponding test loads.


{| border="1px" style="border-collapse:collapse"
|+ '''Tabelle''': Method, ball diameter and load levels depending on the thickness
! rowspan="2" style="width:100px; background:#DCDCDC" | method
! rowspan="2" style="width:130px; background:#DCDCDC" | Ball diameter (mm) 
! colspan="3" style="width:200px; background:#DCDCDC" | load (N)
! rowspan="2" style="width:120px; background:#DCDCDC" | specimen thickness (mm)  
|-
! style="width:60px; background:#DCDCDC" |preload
! style="width:60px; background:#DCDCDC" |load
! style="width:80px; background:#DCDCDC" |total load
|-
| N<br>normal
|align="center"| 2,5 &plusmn; 0,01
|align="center"| 0,3
|align="center"| 5,4
|align="center"| 5,7
|align="center"| 8–10 (>4)<br>1 to 3 layers
|-
| H<br>high
|align="center"| 1,0 &plusmn; 0,01
|align="center"| 0,3
|align="center"| 5,4
|align="center"| 5,7
|align="center"| 8–10 (>4)<br>1 to 3 layers
|-
| L<br>low
|align="center"| 5,0 &plusmn; 0,01
|align="center"| 0,3
|align="center"| 5,4
|align="center"| 5,7
|align="center"| 8–10 (>4)<br>1 to 3 layers
|-
| M<br>micro
|align="center"| 0,395 &plusmn; 0,005
|align="center"| 0,0083
|align="center"| 0,145
|align="center"| 0,1533
|align="center"| 2 &plusmn; 0,5 (>1)
|}

==Execution and specification of material values==

After the preload has been applied, the test force is applied to a spherical indenter to create a reference plane. This force is 5.4 N for methods N, H and L and 0.145 N for method M. The test load is measured after 30 s under the total test force. The additional indentation depth is measured after 30 s under the total test force applied.

The scale value 0 on the dial gauge corresponds to the maximum indentation and the value 100 to practically no indentation, i.e. very high hardness.

The corresponding International Rubber Hardness Degree (IRHD) can be read off from tables for the indentation depth determined in each case. The hardness scale is chosen so that "0" corresponds to the hardness of a material with [[Elastic Modulus|YOUNG's modulus]] zero and "100" to a material with an infinitely large modulus.

==See also==

*[[Hardness]]
*[[SHORE Hardness|SHORE hardness]]
*[[KNOOP Hardness|KNOOP hardness]]

'''References'''

*[[Grellmann, Wolfgang|Grellmann, W.]], [[Seidler, Sabine|Seidler, S.]] (Eds.): Polymer Testing Carl Hanser Munich (2022) 3rd. Edition, pp. 183 (ISBN 978-1-56990-806-8; E-Book ISBN 978-156990-807-5; see [[AMK-Büchersammlung|AMK-Library]] under A 22)
*ISO 48-2 (2018-08): Rubber, Vulcanized or Thermoplastic – Determination of Hardness – Part 2: Hardness between 10 IRHD and 100 IRHD
*ISO 48 (2010-09): Rubber, vulcanized or thermoplastic – Determination of hardness (hardness between 10 IRHD and 100 IRHD) (withdrawn)
*DIN 53519-1 (1972-05): Testing of elastomers – Determination of indentation hardness of soft rubber (IRHD); hardness testing on standard specimens (withdrawn)
*DIN 53519-2 (1972-05): Testing of Elastomers – Determination of Indentation Hardness of Soft Rubber (IRHD), Hardness Testing on Specimens of Small Dimensions, Micro-testing (withdrawn)