Oluschinski at 08:37, 3 September 2026

2026-09-03T08:37:57Z

← Older revision		Revision as of 10:37, 3 September 2026
Line 38:		Line 38:
	* [[Scratch Resistance\|Scratch resistance]]		* [[Scratch Resistance\|Scratch resistance]]

			==References==
	~~'''~~References~~'''~~

	* ISO 2815 (2003-04): Paints and Varnishes – Buchholz Indentation Test		* ISO 2815 (2003-04): Paints and Varnishes – Buchholz Indentation Test

Oluschinski: Created page with "{{Language_sel|LANG=ger|ARTIKEL=BUCHHOLZ-Härte}} {{PSM_Infobox}} BUCHHOLZ hardness FORCETOC ==Indentation resistance according to BUCHHOLZ== The Buchholz hardness test is used to assess the hardness of polymer coating materials (paints) in accordance with ISO 2815. In this standard, BUCHHOLZ hardness is referred to as “Buchholz indentation resistance” (Eindruckwiderstand nach Buchholz). Fil..."

2025-12-01T06:15:01Z

Created page with "{{Language_sel|LANG=ger|ARTIKEL=BUCHHOLZ-Härte}} {{PSM_Infobox}} <span style="font-size:1.2em;font-weight:bold;">BUCHHOLZ hardness</span> __FORCETOC__ ==Indentation resistance according to BUCHHOLZ== The Buchholz hardness test is used to assess the hardness of polymer coating materials (paints) in accordance with ISO 2815. In this standard, BUCHHOLZ hardness is referred to as “Buchholz indentation resistance” (Eindruckwiderstand nach Buchholz). Fil..."

New page

{{Language_sel|LANG=ger|ARTIKEL=BUCHHOLZ-Härte}}
{{PSM_Infobox}}
<span style="font-size:1.2em;font-weight:bold;">BUCHHOLZ hardness</span>
__FORCETOC__

==Indentation resistance according to BUCHHOLZ==

The Buchholz hardness test is used to assess the [[Hardness|hardness]] of polymer coating materials (paints) in accordance with ISO 2815. In this standard, BUCHHOLZ hardness is referred to as “Buchholz indentation resistance” (Eindruckwiderstand nach Buchholz).

[[File:BUCHHOLZ-Indenter.jpg]]
{|
|- valign="top"
|width="50px"|'''Fig. 1''':
|width="600px"|Schematic illustration of BUCHHOLZ identation test
|}

==Experimental conditions==

The [[Indenter|indenter]] here is a small metal wheel (wheel-shaped cutting edge) with sharp edges in hardened tool steel, as shown in '''Fig. 1'''. The test load is 4.905 N for a duration of 30 s. The length ''l'' of the lens-shaped indentation is evaluated, whereby the dimensionless hardness value is calculated as 100 mm/l. The method is suitable for coating thicknesses in the range of 15 to 35 µm. The penetration depth must be between 5 and 24 µm.

==Testing equipment==

'''Figure 2''' shows commercially available testing devices for determining the BUCHHOLZ hardness.

[[File:buchholz2.jpg|450px]]
{|
|- valign="top"
|width="50px"|'''Fig. 2''':
|width="600px"|BUCHHOLZ hardness tester (a): Type 263 from Erichsen GmbH & Co.KG, Hemer, and (b) from Qualitest Inc., Buffalo, USA
|}

==See also==

* [[Hardness]]
* [[Conventional Hardness Testing|Conventional hardness testing]]
* [[Scratch Hardness|Scratch hardness]]
* [[Instrumented Scratch Testing|Instrumented scratch testing]]
* [[Scratch Resistance|Scratch resistance]]

'''References'''

* ISO 2815 (2003-04): Paints and Varnishes – Buchholz Indentation Test
* Brock, T., Groteklaes, M., Mischke, P., Strehmel, B.: Lehrbuch der Lacktechnologie. Vincentz Network, 5th Edition, Hannover (2017), ISBN 978-3-86630-619-6